DCP reaction sticky polymer waterproofing membrane a wet-laid, product descriptions and product images Overview 1. Introduction DCP reaction sticky wet laid polymer waterproofing membrane is a polymer plate, self-adhesive rubber, non-woven and isolated movie. MAC absorb the advantages of polymer waterproofing membranes and self-adhesive waterproof membrane, so it not only has high performance as peneration resistance, weather resistance, extreme temperature and self-healing capabilities, but also to achieve "skin type" wet-application waterproofing system or waterproofing roof technology. 2, product images Overview Second, product characteristics 1, the film has excellent functional polymer waterproofing membranes and self-adhesive waterproof membrane, excellent physical properties such as high penetration resistance, weather resistance, high and low temperatures and more stable chemical properties. 2, the film may adhere to the concrete, and water are inseparable even in long-term immersion, thereby effectively preventing "leakage" phenomenon, and "skin" type of waterproofing. 3, non-woven fabric reinforced layer, the surface of the plate material non-woven macromolecules, macromolecules reduce distortion table of materials, more smooth, straight roller material to pave the way. 4, simple structure, which can be wet or slippery, no undercoat, not affected by the weather, which saves time for the project. 5, safety and environmental protection, solvent and fuel savings in the construction process, to avoid environmental pollution and fire hazards, and save resources. 6, the best price, the basic need cement mortar layer. 50 thick fine aggregate concrete can be canceled, while the pre-paving anti-adhesion construction on the floor, thus reducing the overall cost of building waterproofing system. Due to simplify the structure, it can greatly accelerate the construction schedule. 7, water works well. Underground engineering, a 1.2 mm MAC waterproof fortification levels can reach the required standard three, the number of key performance indicators MM PM CM XP SM 1 Tensile strength, Mpa ≥10 ≥14 ≥16 ≥14 ≥18 2 Elongation at break / % ≥200 ≥400 ≥550 ≥500 ≥600 3 30 minutes under water tightness 0.3 mpa 0.3 mpa 0.3 mpa 0.3 mpa 0.3 mpa 4 pure conditions adhesion / N / mm 3.0 or damaged membrane 5 hypothermia flexibility / ℃ -20 ℃ -20 ℃ -20 ℃ -20 ℃ -20 ℃ 6 N ??/ mm absolute performance of the membrane with the membrane ≥1.5 ≥1.5 ≥1.5 ≥1.5 ≥1.5 film and aluminum ≥3.0 ≥3.0 ≥6.0 ≥6.0 ≥6.0 7 spalling property / N / mm film and the film after ≥1.0 ≥1.0 ≥1.0 ≥1.0 ≥1.0 film and aluminum ≥1.5 ≥1.5 ≥1.5 ≥1.5 ≥1.5 8 immersion peel strength N / mm ≥1.5 ≥1.5 ≥1.5 ≥1.5 ≥1.5 9 surface peel strength after heat aging / N / mm ≥1.5 ≥1.5 ≥1.5 ≥1.5 ≥1.5 10 heat-resistant self-adhesive 70 ℃, 2 h 11 does not flow viscosity / min ≥15 ≥15 ≥15 ≥15 heat aging elongation at break ≥15 12 /% 70 years 80 years 80 years 80 years 80 years 13 ozone aging (40 ℃ 168 h) 20% 200 页 ah elongation no cracks Fourth, the construction method 1, DCP reaction sticky wet-laid water roll down the level when the filter material in general, grassroots empty shops, fixed. 2, when the building facade structure, combined with in-situ concrete is not level. Combined with mechanical fixation. 3, recording methods, combined with site-specific natural mortality levels. 4, DCP reaction sticky wet-laid waterproofing membrane longitudinal lap welding method, hot melt double seam welding, lap width ≥86 mm, the effective width of the weld is not a small 10 mm; lateral ring butt welding method, the two sides in the same plane The choice facing PEV plastic tape, flame welding, PEV glue width 600 mm, uniforms. 5, according to the direction of the plastic surface, select the first material or tape fixed on the basis of the surface with nails and tape hot melt adhesive material. Application of displacement, high pressure, deformation and mountain tunnel underground culverts and other water conservancy projects. Five, DCP sticky polymer reaction engineering vision wet-laid waterproofing membrane