APF-3000 pressure-sensitive adhesive polymer waterproofing membrane reactive prices I. Introduction and product pictures 1. Introduction APF-3000 pressure-sensitive adhesive reactive polymer waterproofing membrane (PY class) for use in underground waterproofing when the bond strength of membrane and membrane should be not less than 4.0N / mm; peel bond strength should be not less than 1.5 N / mm, retention after flooding 168h should be greater than or equal to 70%; and concrete bond strength should be greater than 1.5 N / mm. 2. Introduction Figure II, APF-3000 pressure-sensitive adhesive reactive waterproofing construction elements 1) a wet-laid method (1) waterproof construction before its projection grassroots eradication and clean. (2) should be fully wet grass, then wipe polymer cement paste, vegetarian pulp thickness of 2mm ~ 3mm. (3) torn off its self-adhesive membrane separation membrane attached to the lower surface of the web shop in the polymer cement paste, while the adjacent side of the web of overlapping firmly bonded. (4) The exhaust air below membrane, so that the pulp web and Prime closely adhered to. (5) 24h ~ 48h (depending on the ambient temperature may be) before the next construction step. 2) dry shop law (1) should be solid grass-roots level, without hollowing, loose, sand, peel and other defects; grassroots condensed water when the inside of the roof structure interface cold and cold regions actually have the steam penetration resistance is less than the desired value, or elsewhere indoor moisture may enter through the roof insulation structure layer, the vapor barrier should be set up should be less than 9% no oil, dust. (2) Brushing primary treatment agent: Stones roll should be adopted before spraying method or roll in the grass surface Brushing primary treatment agent, can be self-adhesive membrane Stones when brushing primary treatment agent to be sticky . Reference amount primary treatment agent is 0.2kg / m2. (3) detail node processing Yang angle, eaves, gutters, pipes and other node parts of the roof should be laid additional layer of waterproofing. (4) self-adhesive membrane before Paving Stones should play a good baseline position, and then through the coil center pipe Φ30 × Zhixin tube 1500mm by two each holding one end of the pipe, to be carried to the web Shop starting end position, and the roll forward unfold around 500mm, lift poke release paper in this section has been playing the good baseline aligned SWING shop, with a press roll from the middle to the sides of the web roll, The lift poke release paper is pulled out, rolled onto the used paper core tube. Facade paving according to the method described above may be a bottom-up paving is complete. Sheet lap width of 60mm ~ 80mm. (5) APF-3000 pressure-sensitive reactive adhesive waterproofing membrane seal received the first application received the first part of metal beads fixed and sealed with sealant. 3) The environmental temperature tone waterproofing membrane meets the following requirements: (1) hot-melt not less than -10 ℃. (2) a wet-laid method should not be less than 5 ℃. (3) dry shop law should not be lower than 10 ℃ when the inside of the roof structure condensation interface cold and cold regions actually have the steam penetration resistance is less than the desired value, or elsewhere indoor moisture may enter through the insulation layer of the roof structure, vapor barrier should be set. Third, underground works 1) of the main structure of underground works should be waterproof concrete. 2) waterproof material impermeability should meet 0.3MPa, 120min impermeable requirements. Coil low temperature flexibility should be -25 ℃. Fourth, the production base of buffalo were workers Zhang Publisher